Diameter: | 1.75mm |
Tolerance: | ±0.02mm |
Material Density | 1.21-1.30g/cm3 |
Tensile strength | 17-18 |
Tensile strength（printed） | ≥30Mpa |
Elongation at break | 4.6-5.3% |
Impact intensity (KJ/M,Izod2) | 1-3 |
Vicat softening point | |
Melting Index(g/10min) | 4-6(190 ℃,2.15kg) |
Melting point | |
Printing temperature | |
Hot Pad temperature | 40-60℃ |
Max Volumetric Speed (m³/s） | 12-17 |